Environmentally friendly PVC cable compound

1.Good plasticization 2.Uniform color 3.No significant impurities 4.Environmently friendly

Environmentally friendly PVC cable compounds are made mainly from PVC resin together with various additives such as non-toxic,pollution-free,multi-functional plasticizer,stabillzer,through mixing,plasticizing and granulation.

1.Application

TYPE	PRODUCT NAME	The max allowable operating temperature of the conductive core	Application
J-70	Environmently friendly PVC insulating compound	70°C	Used for instrument and communication cable which working voltage less than 0.6/1KV
J-90	Environmently friendly PVC insulating compound	90°C	Used for hot resistant wires and cables which working voltage less than 450/750V
J-105	Environmently friendly PVC insulating compound	105°C	Used for wires and cables which working voltage less than 26/35KV
H-70	Environmently friendly PVC jacket compound	70°C	Used for wires and cables which working voltage less than 26/35KV
H-90	Environmently friendly PVC jacket compound	90°C	Used for wires and cables which working voltage less than 26/35KV
HTM-70	70°C transparent and non-toxic VC jacket compound	70°C	Used for speaker cables and other wire and cables which requiring transparent
HTM-90	90°C transparent and non-toxic VC jacket compound	90°C	Used for speaker cables and other wire and cables which requiring transparent

2.Performance indicator 

NO.	TYPE		HTM-70	HTM-90	J-70	J-90	J-105	H-70	H-90
1	Tensile strength  MPa  ≥		12.5	15	15	16	16	15	16
2	Tensile strain at break  ≥		180	180	150	150	150	180	180
3	Thermal deformation  ≤		50	40	40	30	30	50	40
4	Impact brittleness temperature °C		-25	-20	-15	-15	-15	-25	-20
5	Volume resistance at 20°C Ω.m  ≥		1.0x108	1.0x109	1.0x1012	1.0x1012	1.0x1012	1.0x108	1.0x109
6	Volume resistance rate at operation temperature	Test temperature °C			70±1	95±1	95±1
		Volume resistivity Ω.m  ≥			1.0x109	5.0x108	5.0x108
7	Dielectric strength  MV/m  ≥		18	18	20	20	20	18	18
8	Thermal stable time 200°C min		50	80	90	180	80	50	80
9	Properties after thermal aging	Test temperature °C	80±2	100±2	100±2	135±2	135±2	100±2	100±2
		Test time  h	168	240	168	240	168	168	240
		Tensile strength after aging  ≥	12.5	15	15	16	16	15	16
		The max change of elongation	±20	±20	±20	±20	±20	±20	±20
		Tensile strain after aging  ≥	180	180	150	150	150	180	180
		The max change of elongation	±20	±20	±20	±20	±20	±20	±20
		Quality loss after thermal aging g/m2   ≤	20	15	20	20	20	23	15
10	Sb   ≤mg/kg				60	60	60	60	60
11	As   ≤mg/kg				25	25	25	25	25
12	Ba   ≤mg/kg				500	500	500	500	500
13	Cd   ≤mg/kg				50	50	50	50	50
14	Cr    ≤mg/kg				25	25	25	25	25
15	Pb    ≤mg/kg				90	90	90	90	90
16	Hg    ≤mg/kg				25	25	25	25	25
17	Se    ≤mg/kg				60	60	60	60	60